Mold Max 60 High Temperature Resistant (294°C) High Performance Molding Silicone

Mold Max® 60,  is a tin grade Shore 60A silicone formulated for applications requiring high heat resistance (up to 560°F / 294°C). This silicone has low viscosity and cured silicone has very low shrinkage. A and B parts according to their weight 100A & It is mixed in 3D ratio.

The life of the mixture is 40 minutes and the curing time is 24 hours. Tin and tin-lead alloy are used in casting of low melting metals.

General Features

• High temperature resistant, developed for high temperature applications and withstands up to 560°F / 294°C
• It has a low mixing viscosity and the shrinkage of cured silicone is negligible.

IMPORTANT: Gently apply the release agent to all surfaces of the model with a soft brush to apply it thoroughly over the entire area. Then apply fine spray paint and let dry for 30 minutes.

Technical Specifications

• Specific Gravity 1.45 g/cc
• Specific Volume 1.19 m3/kg (19.1 cu. in./lb.)
• Mixture Life 40 minutes
• Curing Time 24 hours
• Shore A Hardness 60
• Tensile Strength: 27.44 Bar (398 psi)
• 100% Module 22.82 Bar (331 psi)
• Retention at Break 132 %
• Die B Breaking Force 63 ply
• Drain Allowance <0.0015 in. / in.
• Mixing Ratio by Volume 1A:1B
• Mixing ratios by weight 100A:3B
• Color: Red
• Usable Temperature (min): -53 °C (-65°F)
• Available Temperature (max.)  293 °C (560 °F)
• Mixture Viscosity 20,000 cps
• Dielectric Strength >500 volts/mile
• Dielectric Constant, 100Hz 3.4
• Power Dissipation Coefficient, 100Hz 0.02
• Volume Resistivity 9 x 1014 ohm/cm
• Thermal Conductivity 0.347 W/M*K